Take you to understand UV curing coatings in one minute
|
Update： 2021-5-17 |
光固化涂料主要指在紫外光照射下迅速交聯(lián)固化的一類新型涂料，通常指從液體樹脂變成固態(tài)干膜的過程。因其高效涂裝固化、低能耗和環(huán)境友好特征，已為世界涂料行業(yè)認可，近年來發(fā)展迅速。
UV cured coating mainly refers to a new type of coating which is quickly cross-linked and cured under ultraviolet (UV) irradiation. It usually refers to the process of changing from a liquid resin to a solid dry film. Because of its high-efficiency curing process, low energy consumption and environment-friendly characteristic, UV cured coating has been globally recognized by the coating industry. It has developed rapidly in recent years.
PART
1
歷史/History
★20世紀60年代由Bayer公司成功商業(yè)化光固化涂料。
UV cured coating was put into commercial production by Bayer in the 1960s.
★2000年全球僅用于家具等木器涂裝的光固化涂料已超過2.2萬噸。
Over 22,000 tons UV cured coating was globally used on wood only for furniture in 2000.
★2010年用于包裝領(lǐng)域的光固化涂料增至5.3萬噸。
Up to 53,000 tons UV cured coatings was used in packaging industry in 2010.
★至今大量應(yīng)用于紙張、塑料、金屬、玻璃、陶瓷等多種基材。
Till date, a huge number of UV cured coatings have been applied on paper, plastic, metal, glass, ceramic and many other substrates.
PART
2
波長/Wavelength
在一般光化學研究和光固化應(yīng)用中有實際意義的是中紫外和近紫外區(qū)的紫外光，通常又劃分為以下三個波段: UV A, UV B 和 UV C。光固化體系常用UV A (315~400nm) 和 UV B (280~315nm)，集成電路制作的光刻技術(shù)常用UV C (200~280nm)。
In general photochemical research and UV curing applications, UV light is usually divided into the following three bands during the mid-ultraviolet and near-ultraviolet regions, including UV A, UV B and UV C. Among them, UV A (315~400nm) and UV B (280~315nm) are commonly used in UV cure system. UV C (200~280nm) is usually applied in lithography technology for integrated circuit production.
PART
3
應(yīng)用/Application
光固化涂料/UV cured coating
光固化油墨/UV cured ink
應(yīng)用于包裝裝潢、印刷、電子 (抗蝕油墨、阻焊油墨、標記油墨) 等。
Used in packaging, printing, electronics (anti-corrosion ink, solder mask ink, marking ink), etc.
光固化膠黏劑/UV cured adhesive
分為結(jié)構(gòu)膠、密封膠、層合膠、壓敏膠等。應(yīng)用于光學鏡頭裝配、水晶工藝品、微電子裝配、金屬和塑料支架接合、一次性醫(yī)療器械、液晶顯示屏裝配、玻璃器皿粘接等。
Divided into structural adhesives, sealants, laminating adhesives, pressure-sensitive adhesives, etc. Used in optical lens assembly, crystal crafts, microelectronic assembly, metal and plastic bracket bonding, disposable medical equipment, LCD display assembly, glassware bonding, etc.
光刻膠/Photoresist
用于光刻術(shù)的感光材料。
Used for photolithography in photosensitive materials.三維激光成型/3D laser forming
20世紀80年代末發(fā)展起來的快速成型技術(shù)，利用激光引發(fā)感光樹脂的聚合，要求感光樹脂低粘度、高固化速度、低收縮、低溶脹、層間黏附相容性好、光敏感度高等。
The rapid prototyping technology was developed in the late 1980s. It uses laser to initiate the polymerization of photosensitive resins. The photosensitive resin must possess low viscosity, high curing speed, low shrinkage, low swelling, good interlayer adhesion compatibility and high photosensitivity.
PART
4
組成/Composition
自由基型光引發(fā)劑 (Free radical photoinitiator) /
陽離子型光引發(fā)劑 (Cationic photoinitiator)
低聚物/Oligomer
活性稀釋劑/Reactive diluent
各種助劑/Various additives
感光組分包括低聚物和活性稀釋劑，占整個配方的90%以上。
Photosensitive part includes oligomer and reactive diluent, which accounts for over 90% of the entire formula.
光固化涂料常用組分/
Common components of UV cured coatings
南通新納希新材料有限公司已具備10余年脂環(huán)族環(huán)氧樹脂生產(chǎn)經(jīng)驗，生產(chǎn)能力穩(wěn)定，產(chǎn)品質(zhì)量可靠，致力于為客戶提供優(yōu)質(zhì)服務(wù)，歡迎海內(nèi)外客戶來電垂詢！
Nantong Synasia New Material Co., Ltd. has more than 10 years of experience in the production of cycloaliphatic epoxy resins. We are committed to providing customers with stable production capacity, reliable product quality and considerate service. Welcome customers at home and abroad to contact us!
上一條： Application of cycloaliphatic epoxy resin in UV cationic light curing (2) 下一條： Understand the carbon fiber filament winding technology